高炉、热风炉用低蠕变高铝砖_宜兴市海科窑炉工程有限公司

高炉、热风炉用低蠕变高铝砖系我厂采用优质高铝矾土，添加抗蠕变改性材料经高压成型高温烧成生产的适用于高炉、热风炉炉膛内衬的低蠕变耐火材料。
Low creep high-alumina brick whose raw material is excellent high-alumina bauxite and anti-creep modified material is produced by means of high pressure formation and high temperature burning , which can be used as low creep refractory of the inner lining of blast furnace and hot-blast stove .

指标/牌号	低蠕变高铝砖			复合莫来石砖	堇青石砖	低蠕变粘土砖		致密粘土砖
指标/牌号	H-HD	H-HL	H-LL	H-LLG	H-JL	H-HN	H-LN	H-VN
Al₂O₃ %	80±5	75±5	65±5	65±5	55±5	42±5	40±5	42±5
Fe₂O₃ %	≤1.5	≤1.5	≤1.5	≤1.0	≤1.5	≤1.5	≤2.0	≤1.5
MgO %						≤2.0
显气孔率 %	≤21	≤20	≤21	≤20	≤25	≤22	≤24	≤16
体积密度 g/cm³	2.7	2.7	2.6	2.6	2.3	2.2	2.1	2.3
常温耐压强度Mpa	≥55	≥60	≥55	≥70	≥40	≥40	≥30	≥45
耐火度℃	≥1850	≥1790	≥1790	≥1790		≥1750	≥1730	≥1750
荷重软化温度0.2Mpa ℃		≥1600	≥1600	≥1600	≥1400	≥1400	≥1350	≥1400
蠕变率%(50h)	1500℃≤0.8	1400℃≤0.6	1300℃≤0.8			1200℃≤1.0	1100℃≤1.0
热震稳定性次数	≥6	≥6	≥25	1200℃≥20
热膨胀率%			1300℃≤0.8
重烧线变化率%2h		1500℃ ±0.1	1500℃ ±0.1		1450℃ ±0.2	1450℃ 0-0.4	1450℃ 0-0.3	1450℃ 0-0.4